亚热带区环氧砂浆与混凝土黏结性能试验研究

doi:10.3969/j.issn.1674-0696.2014.05.10

重庆交通大学学报（自然科学版） ›› 2014, Vol. 33 ›› Issue (5): 47-50.DOI: 10.3969/j.issn.1674-0696.2014.05.10

亚热带区环氧砂浆与混凝土黏结性能试验研究

晏国泰，谢金齐，黄镇，陈新林

武汉二航路桥特种工程有限责任公司，湖北武汉 430071

收稿日期:2013-04-11 修回日期:2013-09-02 出版日期:2014-10-15 发布日期:2015-03-10
作者简介:晏国泰（1984—），男，湖南新化人，工程师，主要从事桥梁加固与维修方面的工作。E-mail:155356916@qq.com。

Epoxy Mortar and Concrete Bonding Performance of Subtropical Area

Yan Guotai, Xie Jinqi, Huang Zhen, Chen Xinlin

CCCC Road & Bridge Special Engineering Co. Ltd., Wuhan 430071, Hubei, China

Received:2013-04-11 Revised:2013-09-02 Online:2014-10-15 Published:2015-03-10

摘要/Abstract

摘要： 为确保亚热带气候区桥面铺装施工中薄层环氧砂浆与混凝土梁体之间的黏结质量，对不同环氧砂浆在不同施工工艺条件下进行了对比试验研究。研究表明：环氧砂浆底胶由于强光暴晒老化，影响其黏结强度，随着暴晒时间的延长，黏结强度明显降低；对暴晒过的底胶表层打磨清洗后，可以消除阳光暴晒的影响；采用免底胶环氧砂浆施工可保证黏结强度。

关键词: 桥梁工程, 环氧砂浆, 黏结性能, 试验研究, 亚热带气候区

Abstract: Comparison tests and studies of different epoxy mortar were conducted under different working conditions, in order to ensure the bonding performance between the thin epoxy mortar grout layer and concrete bridge beams in the bridge deck pavement engineering at sub-tropical areas. The results show that the bonding strength of the primer of epoxy mortar will be affected when it is exposed to the strong sunshine; with the increase of exposure time, the bonding strength decreases significantly. However, the influence of exposure under the sunshine can be erased by grinding and cleaning the exposed primer surface. Moreover, the application of epoxy mortar without primer can ensure the bonding strength.

Key words: bridge engineering, epoxy mortar grout, adhesive properties, experimental investigations, subtropical climate

中图分类号:

U445.7+2

晏国泰，谢金齐，黄镇，陈新林. 亚热带区环氧砂浆与混凝土黏结性能试验研究[J]. 重庆交通大学学报（自然科学版）, 2014, 33(5): 47-50.

Yan Guotai, Xie Jinqi, Huang Zhen, Chen Xinlin. Epoxy Mortar and Concrete Bonding Performance of Subtropical Area[J]. Journal of Chongqing Jiaotong University(Natural Science), 2014, 33(5): 47-50.

参考文献

［1］谢业明,潘荣,彭勃.不同固化体系下环氧结构胶的耐湿热老化性能研究［J］.工程与建设,2009,23（1）:55-57.
Xie Yeming,Pan Rong,Peng Bo.Research wet and heat aging resistance of epoxy structural adhesive under different curing system ［J］.Engineering and Construction,2009,23(1):55-57.
［2］潘东芳,彭勃.工艺参数对低粘度建筑结构胶粘结强度的影响［J］.热固性树脂,2004,19(2):24-26.
Pan Dongfang,Peng Bo.Influence of process parameters on the low viscosity structural adhesive strength ［J］.Thermosetting Resin,2004,19(2):24-26.
［3］凌彩珠,宁金成,彭勃.碳纤维加固用胶黏剂工作性能的研究［J］.重庆交通大学学报:自然科学版,2011,30(4):773-777.
Lin Caizhu,Ning Jincheng,Peng Bo.Study on working performance of adhesives for CFRP ［J］.Journal of Chongqing Jiaotong University:Natural Science,2011,30 (4):773-777.
［4］ DL/ T 5193—2004 环氧树脂砂浆技术规程［S］.北京:中国电力出版社,2004.
DL/T 5193—2004 Epoxy Resin Mortar Technology Procedures ［S］.Beijing:China Electric Power Press,2004.
［5］ Bhavesh G K,Raman P S,Nakamura T.Degradation of carbon fiber-reinforced epoxy composites by ultraviolet radiation and condensation ［J］.Journal of Composite Materials,2002,36(24):2713-2733.
［6］ Singh R P,Namrata S T,Bhadraiah S V.Photo-oxidation studies on polyurethane coating:effect of additives on yellowing of polyurethane ［J］.Polymer Degradation and Stability,2001,73(3):443-446.
［7］ Nve B D,Shanahan M E R.Effects of humidity on an epoxy adhesive ［J］.International Journals of Adhesion and Adhesive,1992,12(3):191-196.
［8］林明,侯学杰,王满昌,等.阳光暴晒对环氧树脂基复合材料涂层附着性能的影响［J］.材料开发与应用,2011(12):42-44.
Lin Ming,Hou Xuejie,Wang Manchang,et al.Effect of sun exposure on the properties of epoxy resin matrix composite coating adhesion ［J］.Development and Application of Materials,2011(12):42-44.
［9］ Oteino-Alego V.Characterization of the moisture absorption and thermal ageing behavior of polymeric composite systems using ramen［M］//Ageing Studies and Lifetime Extension of Materials.Germany:Springer-Verlag,1999:113-121.
［10］黄明,黄卫东.环氧沥青固化剂的一些相关问题研究［J］.重庆交通大学学报:自然科学版,2009,28(5):883-886.
Huang Ming,Huang Weidong.Several relative problems of epoxy asphalt solidifiers ［J］.Journal of Chongqing Jiaotong University:Natural Science,2009,28(5):883-886.

[1]	周建庭1,2，黎娅2，张洪2，夏润川2，杨文琦2. 基于自发漏磁检测的钢绞线两点腐蚀试验研究[J]. 重庆交通大学学报（自然科学版）, 2021, 40(07): 74-81.
[2]	张华1，张正琦2 ，程高3，4，田伯科1. 黄土地区陡崖坡段桩基合理临坡距研究[J]. 重庆交通大学学报（自然科学版）, 2021, 40(07): 93-98.
[3]	刘金春，宋子轩，梁栋. 单箱三室连续梁桥在横向温度梯度与汽车偏载下的空间效应分析[J]. 重庆交通大学学报（自然科学版）, 2021, 40(06): 80-86.
[4]	郑植1,2，耿波2，袁佩2，李嵩林2，胡正涛3. 桥墩复合材料防船撞装置新型连接试验研究[J]. 重庆交通大学学报（自然科学版）, 2021, 40(05): 66-73.
[5]	张阳1，屈少钦1，卢九章2，霍文斌3. UHPC纤维定向法及对受拉性能影响[J]. 重庆交通大学学报（自然科学版）, 2021, 40(05): 74-80.
[6]	董玉文1，余鑫2，秦瑶1,王宗波1. 冻融与锈蚀作用对钢筋混凝土黏结性能的影响[J]. 重庆交通大学学报（自然科学版）, 2021, 40(05): 81-86.
[7]	傅立磊. 基于随机激励响应的参数识别相关函数法[J]. 重庆交通大学学报（自然科学版）, 2021, 40(04): 70-75.
[8]	苏小波1，肖林2. 空间刚架结构钢-混结合段合理构造模型试验和数值模拟研究[J]. 重庆交通大学学报（自然科学版）, 2021, 40(04): 76-82.
[9]	梁宗保1，柴洁1，纳守勇2，马天立1，唐玉1. 基于深度学习的桥梁健康监测数据有效性分析[J]. 重庆交通大学学报（自然科学版）, 2021, 40(03): 78-83.
[10]	唐启智1,辛景舟1,2,周建庭1,付雷1,3,张俊4. 基于时序分析的锈蚀RC拱损伤识别：仿真与验证[J]. 重庆交通大学学报（自然科学版）, 2021, 40(02): 69-77.
[11]	戎贤1,2，杨洪渭1，张健新1,2. 带钢端头的装配式混凝土梁柱中节点滞回性能试验研究[J]. 重庆交通大学学报（自然科学版）, 2021, 40(02): 78-82.
[12]	刘小会，许杨，陈思甜，徐略勤. 人行悬索桥地震响应分析[J]. 重庆交通大学学报（自然科学版）, 2021, 40(01): 65-71.
[13]	琚利平1，王银辉2，陆晓宏3，单继栋4. 行车落物作用下钢筋混凝土箱梁破坏形态分析[J]. 重庆交通大学学报（自然科学版）, 2021, 40(01): 72-78.
[14]	王桢1,2，周建庭1,3，张劲泉1,4，吴海军1，吴月星1. 现浇分段长度对万吨级平转斜拉桥受力的影响分析[J]. 重庆交通大学学报（自然科学版）, 2020, 39(12): 44-52.
[15]	郝宪武，舒鹏，郝键铭. 大跨度非对称悬索桥的静风稳定性研究[J]. 重庆交通大学学报（自然科学版）, 2020, 39(12): 53-59.

亚热带区环氧砂浆与混凝土黏结性能试验研究

Epoxy Mortar and Concrete Bonding Performance of Subtropical Area

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics