乳化沥青的界面黏弹性及Zeta电位研究

doi:10.3969/j.issn.1674-0696.2017.01.08

摘要/Abstract

摘要： 通过对两种自制乳化剂A，B界面扩张模量及所制备乳化沥青Zeta电位的测定，考察了界面扩张模量和Zeta电位与乳化沥青稳定性之间的关系。当自制乳化剂A，B浓度分别为100mg/L，50mg/L时，界面膜弹性最大。当乳化剂A，B掺量分别为2.8%、1.2%时，所制备乳化沥青Zeta电位绝对值最大，储存稳定性最佳。因此，界面扩张模量、Zeta电位与乳化沥青储存稳定性有着良好的对应关系，故二者可作为评价乳化剂优劣及确定乳化剂最佳用量的指标。

关键词: 道路工程, 界面扩张流变, Zeta电位, 储存稳定性

Abstract: The relationship among interfacial dilatational modulus, zeta potential and the stability of emulsified asphalt was investigated by measuring interfacial dilatational modulus and zeta potential of self-made emulsifier A and B. When the concentration of self-made emulsifier A and B was 100 mg/L and 50 mg/L respectively, the elasticity of interfacial film was the largest. When the dosage of emulsifier A and B was 2.8% and 1.2% respectively, the emulsified asphalt presented the maximum Zeta potential absolute value and the best storage stability. Thus, the interfacial dilatational modulus and zeta potential has a good correspondence to the storage stability of emulsified asphalt, so both can be used as an indicators of evaluation of the emulsifier merits and determination of emulsifier optimal dosage.

Key words: highway engineering, interfacial dilational rheology, zeta potential, storage stability

中图分类号:

U214.7

裴强，杜素军，庞瑾瑜. 乳化沥青的界面黏弹性及Zeta电位研究[J]. 重庆交通大学学报（自然科学版）, 2017, 36(1): 42-45.

PEI Qiang, DU Sujun, PANG Jinyu. The Study on the Interfacial Viscoelasticity and Zeta Potential of Emulsified Asphalt[J]. Journal of Chongqing Jiaotong University(Natural Science), 2017, 36(1): 42-45.

参考文献

［1］ RAMIREZ P, PEREZ L M，TRUJILLOA L A，et al. Equilibrium and surface rheology of two polyoxyethylene surfactants differing in the number of oxyethylene groups［J］.Colloids & Surfaces A Physicochemical & Engineering Aspects，2011，375（1/2/3）：130-135.
［2］ NOSKOV B A, LOGLIO G，MILLER R. Dilational surface viscoelasticity of polyelectrolyte/surfactant solutions: formation of heterogeneous adsorption layers［J］. Advances in Colloid and Interface Science,2011，168（1/2）：179-197.
［3］王玮，李楷，郝帅，等.结合吸附模型预测油水液滴的界面流变性质［J］.化工学报，2013，64（8）：2947-2955.
WANG Wei, LI Kai, HAO Shuai, et al. Interfacial rheological properties of oil/water droplet with dynamic adsorption models［J］.CIESC Journal,2013，64（8）：2947-2955.
［4］ STUBENRAUCH C, MILLER R. Stability of foam films and surface rheology: an oscillating bubble study at low frequencies［J］. Jourual of Physical Chemistry B, 2004，108（20）：6412-6421.
［5］孙涛垒，张路，王宜阳，等.界面张力弛豫法研究不同分子量原油活性组分界面扩张黏弹性［J］.高等学校化学学报，2003，24（12）：2243-2247.
SUN Taolei, ZHANG Lu, WANG Yiyang, et al. Studies on interfacial dilational visoelasticity of active constituents in crude oil with different molecular weights by interfacial tension relaxation methods［J］. Chemical Journal of Chinese Universities,2003，24（12）：2243-2247.
［6］ BLOMQVIST B R, WARNHEIM T，CLAESSON P M. Surface rheology of PEO-PPO-PEO triblock copolymers at the airwater interface: comparison of spread and adsorbed layers［J］. Langmuir,2005，21（14）：6373-6384.
［7］刘宏生，韩培慧，孙刚，等.非离子Gemini表面活性剂的表/界面扩张性质［J］.大庆石油地质与开发，2012，31（6）：156-160.
LIU Hongsheng, HAN Peihui, SUN Gang, et al. Surface/interface expanding properties of non-ionic Gemini surfactant［J］. Petroleum Geology and Oilfield Development in Daqing,2012，31（6）：156-160.
［8］窦立霞，郭龙，王红艳，等.油/聚合物溶液体系动态界面扩张模量的测量［J］.油田化学，2004，21（1）：72-74.
DOU Lixia, GUO Long, WANG Hongyan, et al. Measurement of dynamic interfacial dilatational modulus between oil and polymer solution［J］. Oilfield Chemistry,2004，21（1）：72-74.
［9］曹绪龙，崔晓红，李秀兰，等.扩张流变法研究表面活性剂在界面上的聚集行为［J］.化学通报，2009，72（6）：507-515.
CAO Xulong, CUI Xiaohong, LI Xiulan, et al. Study on the aggregation behavior of surfactant at interface by the dilatational rheological methods［J］. Chemistry,2009，72（6）：507-515.
［10］史晓峰.线型及支状嵌段聚醚的界面聚集行为［D］.济南：山东大学，2008：19-29.
SHI Xiaofeng. The Interface Aggregation Behavior of Linear and Branch Block Polyether［D］.Jinan: Shandong University,2008：19-29.
［11］ XIAO Liyang, VINCENT J V, PETER K K. Dynamic asphaltene-resin exchange at the oil/water interface: time-dependent W/O emulsion stability for asphaltene/resin model oils［J］. Energy&Fuels，2007，21（3）：1343-1349.
［12］韩璐，楚艳苹，李良君，等.表面活性剂与聚电解质界面扩张黏弹性研究［J］.西华大学学报（自然科学版），2009，28（5）：87-90.
HAN Lu, CHU Yanping, LI Liangjun, et al. Study of interfacial dilational viscoelastic properties between polyelectrolyte and surfactants at water/oil interface［J］. Journal of Xihua University（Natural Science）,2009，28（5）：87-90.
［13］ DANUTA M S, HARVEY W Y. Rheology of asphaltene-toluene/water interfaces［J］. Langmuir,2005，21（25）：11651-11658.
［14］王宜阳，张路，孙涛垒，等.不同结构破乳剂油水界面扩张粘弹性研究［J］.物理化学学报，2003，19（4）：297-301.
WANG Yiyang, ZHANG Lu, SUN Taolei, et al. Influences of demulsifiers with different structures on dilational properties of decane/water interface［J］. Acta Physico-Chimica Sinica，2003，19（4）：297-301.
［15］王宜阳，张路，孙涛垒，等.酸性模拟油的油水界面扩张黏弹性研究［J］.高等学校化学学报，2003，24（11）：2044-2047.
WANG Yiyang, ZHANG Lu, SUN Taolei, et al. Studies on interfacial dilational viscoelasticity properties of acidic simulated oil/alkali-surfactant system［J］. Chemical Journal of Chinese Universities,2003，24（11）：2044-2047.
［16］ ERK K A, MARRIN J D，SCHWALBE J T, et al. Shear and dilational interfacial rheology of surfactant-stabilized droplets［J］. Journal of Colloid and Interface Science,2012，377（1）：442-449.
［17］徐明进，李明远，彭勃，等. Zeta电位和界面膜强度对水包油乳状液稳定性影响［J］.应用化学，2007，24（6）：623-627.
XU MingJin, LI Mingyuan, PENG Bo, et al. Effects of strength of interfacial film and zeta potential on oil-in-water emulsion stability［J］. Chinese Journal of Applied Chemisity,2007，24（6）：623-627.
［18］王莉，李丽芳，贾猛猛，等. Zeta电位法选择农药悬浮剂所需润湿分散剂［J］.应用化学，2010，27（6）：727-731.
WANG Li, LI Lifang, JIA Mengmeng, et al. Selection of wetting dispersant in pesticide suspension concentrate with zeta potential method［J］. Chinese Journal of Applied Chemisity,2010，27（6）：727-731.
［19］惠会清.乳化沥青储存及使用性能影响因素分析研究［J］.山西交通科技，2005（4）：22-23.
HUI Huiqing. The influencing factor analysis of emulsified asphalt storing and its usage performance［J］. Shanxi Science & Technology of Communications, 2005(4):22-23.

[1]	张淑宝. 一种中央分隔带分离式改进混凝土护栏的研究[J]. 重庆交通大学学报（自然科学版）, 2021, 40(07): 107-111.
[2]	赵伟. 纳米蒙脱石/SBS复掺改性沥青性能试验研究[J]. 重庆交通大学学报（自然科学版）, 2021, 40(07): 118-122.
[3]	郭鹏1，陈思贤1，曹志国1，刘俊1，孟建玮2，鲜江林3. 复配废机油再生剂的制备及性能研究[J]. 重庆交通大学学报（自然科学版）, 2021, 40(06): 87-91.
[4]	肖庆一1,2，赵鹏1，孙博伟3，张怡4，丁啸5. 废植物油再生沥青结合料性能研究[J]. 重庆交通大学学报（自然科学版）, 2021, 40(06): 92-98.
[5]	何丽红1,2,温仙仙1,2,侯艺桐1,2,邓稳1,2. 阴离子乳化沥青粒径大小及分布影响因素分析[J]. 重庆交通大学学报（自然科学版）, 2021, 40(06): 99-104.
[6]	姚爱玲1，王军伟2，许敏3，杨孟乾4，杨涛1. 水泥稳定碎石基层沥青路面隆起开裂数值分析[J]. 重庆交通大学学报（自然科学版）, 2021, 40(06): 105-111.
[7]	赵全满，任瑞波，刘瑶，李志刚，户桂灵. 城市道路检查井井周路面破坏机理[J]. 重庆交通大学学报（自然科学版）, 2021, 40(05): 87-94.
[8]	王志祥1,2，李建阁1，陈楚鹏2. 基于变权重评价的沥青路面使用性能灰色预测[J]. 重庆交通大学学报（自然科学版）, 2021, 40(05): 95-101.
[9]	肖庆一1，2，3，封仕杰1，孙立东1，陈向伟1. 碱渣掺量对不同龄期下半刚性再生基层力学性能研究[J]. 重庆交通大学学报（自然科学版）, 2021, 40(05): 102-109.
[10]	潘兵宏1，2，任卉2，单慧敏1，霍永富1. 客货分离整体式路基互通出口同分带开口长度研究[J]. 重庆交通大学学报（自然科学版）, 2021, 40(04): 83-90.
[11]	孔令云1，邹胜楠1，黄麟钬2，吴海鹰3，余苗1，杨博1. 复合式路面疲劳裂纹扩展数值模拟研究[J]. 重庆交通大学学报（自然科学版）, 2021, 40(04): 91-97.
[12]	凌天清1，魏巧2，李传强3，袁海2，杨清尘3. 生物柴油-塑料裂解蜡复合温拌改性沥青性能研究[J]. 重庆交通大学学报（自然科学版）, 2021, 40(04): 98-104.
[13]	王清洲1，孙超1，檀奥龙2，魏连雨1. 膨胀性泥岩重塑土膨胀力试验研究[J]. 重庆交通大学学报（自然科学版）, 2021, 40(04): 112-117.
[14]	王民1,2，尚飞1，肖丽1，包广志3. 钢桥面浇注式沥青铺装复合梁疲劳损伤规律分析[J]. 重庆交通大学学报（自然科学版）, 2021, 40(03): 84-88.
[15]	董仕豪，韩森，尹媛媛，吴松，张启鑫. 基于表面能理论的石灰改性沥青黏附性研究[J]. 重庆交通大学学报（自然科学版）, 2021, 40(03): 89-97.