柔性纤维混凝土疲劳性能试验研究

doi:10.3969/j.issn.1674-0696.2026.09.08

摘要/Abstract

摘要： 针对疲劳试验应力水平分级细、试样数量多、试验周期长、花费高的现实和柔性纤维混凝土（FFRC）疲劳系统试验数据欠缺的现状，针对体积掺量为0.15%的FFRC和普通混凝土分别开展了静力弯拉试验和弯拉疲劳试验，并采用回归分析得到了疲劳方程。试验结果表明：在0.75与0.65应力水平下，FFRC相对疲劳寿命分别达到普通混凝土的7.53倍和29.60倍，在0.65应力水平下，疲劳寿命的提高程度尤为显著；疲劳方程显示，若失效概率分别为0.1、0.3和0.5，疲劳寿命分别为200万次、150万次、100万次时，FFRC疲劳强度对应应力水平分别为0.564、0.569、0.575，0.557、0.564、0.574和0.556、0.566、0.580，而普通混凝土疲劳强度对应应力水平分别为0.539、0.544、0.550，0.550、0.555、0.563和0.537、0.544、0.554，FFRC的疲劳强度显著提高。研究结果可为FFRC的理论设计与工程应用提供依据。

关键词: 道路工程；柔性纤维；纤维混凝土；疲劳寿命；疲劳方程

Abstract: In response to the reality of fine grading of stress levels, large number of specimens, long test cycles, and high costs in fatigue testing, as well as the lack of fatigue system test data for flexible fiber reinforced concrete (FFRC), static flexural tests and flexural fatigue tests on FFRC with a volume fraction of 0.15% and on plain concrete was respectively conducted, and fatigue equations were obtained through regression analysis. The experimental results show that at stress levels of 0.75 and 0.65, the relative fatigue life of FFRC reaches 7.53 and 29.6 times that of plain concrete, respectively, and the improvement in fatigue life is particularly significant at the 0.65 stress level. The fatigue equations show that if the failure probabilities are 0.1, 0.3 and 0.5 respectively, and the fatigue lives are 2 million times, 1.5 million times and 1 million times respectively, the stress levels corresponding to the fatigue strength of FFRC are 0.564, 0.569 and 0.575, 0.557, 0.564 and 0.574, as well as 0.556, 0.566 and 0.580, respectively. While the stress levels corresponding to the fatigue strength of ordinary concrete are 0.539, 0.544 and 0.550, 0.555and 0.563, as well as 0.537, 0.544 and 0.554, respectively. Therefore, the fatigue strength of FFRC is significantly improved. The research results can provide a basis for the theoretical design and engineering application of FFRC.

Key words: road engineering; flexible fiber; fiber-reinforced concrete; fatigue life; fatigue equation

中图分类号:

U466
O319.56

易志坚1，张拓1，李亚1，谷建义1，董明思2. 柔性纤维混凝土疲劳性能试验研究[J]. 重庆交通大学学报（自然科学版）, 2026, 45(9): 66-71.

Yi Zhijian1, Zhang Tuo1, Li Ya1, Gu Jianyi1, Dong Mingsi2. Experimental research on fatigue performance of flexible fiber-reinforced concrete[J]. Journal of Chongqing Jiaotong University(Natural Science), 2026, 45(9): 66-71.

/ 推荐

参考文献

［1］梁宁慧，毛金旺，游秀菲，等.多尺度聚丙烯纤维混凝土弯曲疲劳寿命试验及数值模拟［J］. 材料导报, 2024, 38 (4): 22040023.
Liang Ninghui, Mao Jinwang, You Xiufei, et al. Flexural fatigue life test and numerical simulation of multi-scale polypropylene fiber reinforced concrete［J］. Materials Reports, 2024, 38(4): 22040023.
［2］张鲜维，柴军瑞，覃源，等.聚丙烯纤维和织物混凝土的发展及力学性能研究［M］.北京：中国水利水电出版社，2019.
Zhang Xianwei, Chai Junrui, Qin Yuan, et al. Development and mechanical properties of polypropylene fiber and fabric concrete［M］. Beijing: China Water & Power Press, 2019.
［3］陈先华. 土木工程材料学［M］. 南京: 东南大学出版社, 2021.
Chen Xianhua. Civil engineering materials science［M］. Nanjing: Southeast University Press, 2021.
［4］ Pakravan H R, Ozbakkaloglu T. Synthetic fibers for cementitious composites: a critical and in-depth review of recent advances［J］. Construction and Building Materials, 2019, 207: 491-518.
［5］夏智.聚丙烯纤维混凝土基本力学性能试验研究［J］.武汉理工大学学报（交通科学与工程版），2025，49(1): 135-141.
Xia Zhi. Experimental study on basic mechanical properties of polypropylene fiber concrete ［J］. Journal of Wuhan University of Technology (Transportation Science & Engineering), 2025，49(1): 135-141.
［6］陈舣亦, 赵凤杰, 易志坚, 等. 柔性纤维砼特殊路用性能研究［J］. 重庆交通大学学报（自然科学版）, 2005, 24(1): 42-45.
Chen Yiyi, Zhao Fengjie, Yi Zhijian, et al. Research of special peculiarity of flexible fiber reinforced concrete［J］. Journal of Chongqing Jiaotong University (Natural Science), 2005, 24(1): 42-45.
［7］车承志, 易志坚, 何小兵, 等.柔性纤维砼断裂韧性的试验研究［J］. 重庆交通大学学报（自然科学版）, 2006, 25(4): 62-64.
Che Chengzhi，Yi Zhijian，He Xiaobing，et al. Experimental research on fracture toughness of flexible fiber reinforced concrete ［J］. Journal of Chongqing Jiaotong University (Natural Science), 2006, 25(4): 62-64.
［8］ Kudoli A B, Patil R S, Yeole M M. Recent advances in polypropylene fibre-reinforced concrete: a systematic review on mechanical characteristics and durability performance［J］. Journal of Mines, Metals and Fuels, 2025: 2887-2896.
［9］ Yang Zhengxian, Zheng Zelong, Xu Pu, et al. Effect of synthetic fibers on early and long-term performance of UHPC: a review［J］. Journal of Building Engineering, 2025, 101: 111850.
［10］ Liu Junyu, Liu Xi. Fiber-reinforced concrete for complex engineering conditions: material properties, nonlinear response and sustainable applications in spaceflight［J］. High Temperature Materials and Processes, 2026, 45: 20250102.
［11］ Wei Zhang. Conclusions and future research directions［M］∥Civil and Structural Engineering, Fiber Reinforced Polymer Reinforcement of Concrete Structures.Woodhead Publishing, 2026:409-423.
［12］ Dinitz A M, Stenko M S. The successful use of thin polysulfide epoxy polymer concrete overlays on concrete and steel orthotropic bridge decks［C］∥Senapathi S, Casey K, Hoit M. Structures Congress 2010. Reston，USA: American Society of Civil Engineers, 2012: 530-540.
［13］ Pranav S, Lahoti M, Muthukumar G, et al. A comprehensive review on applications of engineered cementitious composites in pavements［J］. Construction and Building Materials, 2023, 409: 134056.
［14］张书, 马睿, 胡昱, 等. 基于应力应变疲劳准则的混凝土疲劳寿命分析［J］. 清华大学学报(自然科学版), 2024, 64(8): 1330-1335.
Zhang Shu, Ma Rui, Hu Yu, et al. Analysis of concrete fatigue life based on stress-strain fatigue criterion［J］. Journal of Tsinghua University (Science and Technology), 2024, 64(8): 1330-1335.
［15］余一凡. 复杂荷载与环境作用下混凝土梁使用寿命预测研究［D］. 杭州: 浙江大学, 2024.
Yu Yifan. Study on life prediction of reinforced concrete beams under complex loads and environmental actions［D］. Hangzhou: Zhejiang University, 2024.
［16］ CuiKai, Xu Lihua, Feng Ran, et al. Fatigue damage evolution of polypropylene fiber reinforced concrete under uniaxial cyclic compression［J］. Composite Structures, 2026, 378: 119914.
［17］ Cui Kai, Xu Lihua, Zhou Zhanpeng, et al. Tensile behavior of polypropylene fiber reinforced concrete under uniaxial constant-amplitude cyclic loading: fatigue properties and probabilistic fatigue life model［J］. Journal of Building Engineering, 2026, 117: 114777.
［18］ ZhangPu, Hou Jingwen, Zhang Dong, et al. Enhancing the fatigue behavior of fiber-reinforced concrete with a ternary multiscale hybrid fiber system and its damage evolution［J］. Journal of Building Engineering, 2026, 130: 117013.
［19］ Hait P, Karthik R, Mitra R, et al. Natural and artificial fibre reinforced concrete: a state-of-art review［J］. International Journal of Engineering, Transactions A: Basics, 2024, 37(3):503-510.
［20］姚武, 李杰, 周钟鸣. 聚丙烯纤维对混凝土抗拉强度的影响［J］. 混凝土, 2001(10): 40-42.
Yao Wu, Li Jie, Zhou Zhongming. Influence of polypropylene fiber on the tensile strength of concrete［J］. Concrete, 2001(10): 40-42.
［21］ Li Yaxiong, Chen Meng, Zhang Tong, et al. Behavior of hybrid steel and recycled polymer fibers reinforced rubberized concrete under flexural fatigue loading［J］. Construction and Building Materials, 2024, 456: 138936.
［22］姚祖康. 公路设计手册-路面［M］. 2版. 北京: 人民交通出版社, 1999.
Yao Zukang. Highway design manual-pavement［M］. 2nd ed. Beijing: China Communications Press, 1999.
［23］ Weibull W. A statistical theory of strength of materials［J］. Proceedings of the Royal Academy of Engineering, Science, 1939, 151：5-45.
［24］ Olsson K E. Weibull analysis of fatigue test data［J］. Quality and Reliability Engineering International, 1994, 10(5): 437-438.
［25］ Romualdi J P, Batson G B. Behavior of reinforced concrete beams with closely spaced reinforcement［J］. Journal Proceedings, American Concrete Institute, 1963, 60(6): 775-789.
［26］ Yang Junchao, Zhang Yuanhang, Huang Jian. The strengthening theory of steel fiber reinforced concrete and its application in tunnel engineering: a review［J］. Journal of Engineered Fibers and Fabrics, 2024, 19: 1-17.
［27］ Martinello Carlesso D, Cavalaro S H P, Bairán, J M, et al. Flexural fatigue performance of pre-cracked steel fibre reinforced concrete: experimental program and design-oriented approach［J］. Construction and Building Materials, 2025, 467: 140308.
［28］ Adel M, Li Wang, Xiao Yan, et al. Fatigue-dependent pull-out degradation of inclined hooked-end steel fibers in SFRCC: experiments and mechanics-based modeling［J］. Cement and Concrete Research, 2025, 197: 107962.
［29］ Hussain M Z, Shah S Z H, Choudhry R S, et al. Fatigue life enhancement of fiber-reinforced composites: a state-of-the-art review and outlook［J］. Results in Engineering, 2025, 28: 108125.
［30］易志坚，杨庆国，李祖伟，等.基于断裂力学原理的纤维砼阻裂机理分析［J］.重庆交通大学学报（自然科学版），2004，23(6): 43-45.
Yi Zhijian, Yang Qingguo, Li Zuwei, et al. Use of fracture mechanics concept to interpret crack resistance behavior of fiber reinforced concrete［J］. Journal of Chongqing Jiaotong University (Natural Science), 2004, 23(6): 43-45.