RAP粒径对热再生沥青混合料性能的影响研究

doi:10.3969/j.issn.1674-0696.2020.06.13

摘要/Abstract

摘要： 为研究RAP粒径对热再生沥青混合料性能的影响，采用毛体积密度和马歇尔稳定度指标，对新旧沥青融合性进行评价，得到新旧沥青融合性较好的拌合工艺。改变基准料中细RAP比例，采用马歇尔试验、车辙试验、低温小梁弯曲试验和冻融劈裂试验，研究不同细RAP比例对再生沥青混合料体积指标、力学指标和路用性能的影响。研究结果表明：“再生干拌法”能提高再生沥青混合料中新旧沥青的融合性和混合料拌合的均匀性，提高再生沥青混合料性能；再生沥青混合料毛体积密度和马歇尔稳定度随细RAP比例升高出现峰值，基准料中细RAP比例达到13%时，再生沥青混合料毛体积密度最大，细RAP比例达到17.5%时，再生沥青混合料马歇尔稳定度最大；随着细RAP比例增加，再生沥青混合料路用性能出现峰值，细RAP掺量超过13%时，再生沥青混合料路用性能开始下降，高比例细RAP会导致再生沥青混合料缺少自由细矿料填充空隙，再生沥青混合料性能下降；用灰色关联度分析法设计的基准料组合能有效弥补高RAP掺量对再生沥青路面带来的不利影响。

关键词: 道路工程, 热再生, 基准料, 融合性, 路用性能

Abstract: To study the influence of RAP (Recycled Asphalt Pavement) particle size on the properties of hot recycled asphalt mixture, the gross bulk density and Marshall stability index were selected to evaluate the fusion of new and old asphalt, and a better mixing process was obtained. The ratio of fine RAP in the reference material was changed. Marshall test, rutting test, low temperature trabecular bending test and freeze-thaw split test were used to study the influence of different fine RAP ratios on volume index, mechanical index and road performance of recycled asphalt mixture. The research results show that the “recycled dry mixing method” can improve the fusion of new and old asphalt and the uniformity of mixture mixing in recycled asphalt mixture, and improve the performance of recycled asphalt mixture. The gross bulk density and Marshall stability index of recycled asphalt mixture have the peak value with the increase of the fine RAP ratio. When the proportion of fine RAP in the reference material reaches 13%, the gross bulk density of recycled asphalt mixture is the largest, and when the ratio of fine RAP reaches 17.5%, the Marshall stability of recycled asphalt mixture is the largest. As the proportion of fine RAP increases, the road performance of recycled asphalt mixture has a peak value. When the fine RAP content exceeds 13%, the road performance of recycled asphalt mixture begins to decline. The high proportion of fine RAP will cause the lack of free fine aggregate to fill the gap, and the performance of recycled asphalt mixture will decline. The reference material combination designed by the grey correlation analysis method can effectively compensate the adverse effects of high RAP content on the recycled asphalt pavement.

Key words: highway engineering, hot recycled, reference materials, fusion, road performance

中图分类号:

U416

程培峰1，向银剑1，李炬辉1，周远智2. RAP粒径对热再生沥青混合料性能的影响研究[J]. 重庆交通大学学报（自然科学版）, 2020, 39(06): 81-86.

CHENG Peifeng1, XIANG Yinjian1 , LI Juhui1, ZHOU Yuanzhi2. Influence of RAP Particle Size on the Performance of Hot Recycled Asphalt Mixture[J]. Journal of Chongqing Jiaotong University(Natural Science), 2020, 39(06): 81-86.

参考文献

［1］霍廷军.SBS改性高RAP掺量热再生混合料温度敏感性及抗裂性能研究［J］.公路工程, 2015, 40(5): 129-133.
HUO Tingjun. Study on the temperature sensitivity and crack resistance of SBS modified high RAP content hot recycled mixture［J］. Highway Engineering, 2015, 40
(5): 129-133.
［2］马翔,倪安琪，李强.旧料对沥青混合料力学特性的影响［J］.公路交通科技, 2015, 32(10): 14-18.
MA Xiang, NI Anqi, LI Qiang. Influence of RAP on mechanical property of asphalt mixture［J］. Journal of Highway and Transportation Research and Development ,
2015, 32(10): 14-18.
［3］李琳,尹玉霞.高比例RAP掺量热再生SMA混合料新旧料融合性及工厂化生产参数研究［J］.公路工程, 2016, 41(4): 232-236.
LI Lin, YIN Yuxia. Research on industrialized parameters and evaluation of blending performance of reclaimed SMA pavementwith high RAP content［J］. Highway
Engineering, 2016, 41(4): 232-236.
［4］朱梦良,孟华君.回收料掺量对沥青混合料马歇尔物理力学指标的影响［J］.长沙理工大学学报（自然科学版）, 2012, 9(2): 7-12.
ZHU Mengliang, MENG Huajun. The content of the recycled asphalt mixture effect on the Marshall volume parameters［J］. Journal of Changsha University of Science
and Technology （Natural Science), 2012, 9(2): 7-12.
［5］秦永春, 黄颂唱, 徐剑，等.厂拌温再生沥青混合料中新旧沥青的融合性研究［J］.公路交通科技, 2015, 32(12): 24-28.
QIN Yongchun, HUANG Songchang, XU Jian，et al. Research of blending performance of virgin and reclaimed asphalt in plant warm recycled asphalt mixture［J］.
Journal of Highway and Transportation Research and Development ,2015, 32(12): 24-28.
［6］徐伟,王勋.再生沥青混合料沥青胶浆微观状态测试方法研究［J］.公路工程, 2014, 39(2):68-71.
XU Wei, WANG Xun. Study on test method of asphalt mastic microstate in recycled asphalt pavement［J］. Highway Engineering, 2014, 39(2): 68-71.
［7］ F BOWERS B, HUANG B S, SHU Xiang, et al. 基于GPC和FTIR 的再生混合料新旧沥青融合程度研究［J］. 张德鹏,徐金枝,郝培文,译.中外公路, 2016, 36(6): 214-219.
F BOWERS B, HUANG B S, SHU Xiang, et al. Investigation of reclaimed asphalt pavement blending efficiency through GPC and FTIR ［J］. ZHANG Depeng, XU Jinzhi, HAO
Peiwen, Translate. Journal of China and Foreign Highway, 2016, 36(6)：214-219.
［8］关泊,张德鹏,李雨，等.基于原子力显微镜的新旧沥青融合机理及力学性质研究［J］.西安建筑科技大学学报(自然科学版), 2017, 49(6): 919-924.
GUAN Bo, ZHANG Depeng, LI Yu, et al. Research on the fusion mechanism and mechanical property of the old and new asphalt based on atomic force microscope［J］.
Journal of Xian University of Architecture and Technology (Natural Science ), 2017, 49(6): 919-924.
［9］NGUYEN H V. Effects of mixing procedures and RAP size on stiffness distribute of hot recycled asphalt mixtures［J］. Construction and Building Materials,
2013, 47: 728-742.
［10］MCDANIEL R S, SOLEYMANI H, ANDERSON R M, et al. Recommended Use of Reclaim Asphalt Pavement in the Superpave Mix Design Method［R］. Washington,
D.C.:Transportation Research Board，2000.
［11］黄康旭,梁星敏,徐波.RAP掺量对泡沫温拌再生沥青混合料路用性能的影响［J］.材料科学与工程学报, 2016, 34(5): 794-797.
HUANG Kangxu, LIANG Xingmin, XU Bo. Influences of RAP dosage on road performances of foamed warm mix reclaimed asphalt［J］. Journal of Materials Science and
Engineering, 2016, 34(5): 794-797.
［12］刘立志.RAP材料厂拌热再生混合料质量控制研究［D］. 重庆：重庆交通大学, 2013.
LIU Lizhi. The Quality Control Research of RAP material Mixing Plant Thermal Regeneration Mixes［D］. Chongqing： Chongqing Jiaotong University, 2013.
［13］郭康升.基于基准料合成的不同掺配率再生混合料路用性能研究［D］. 重庆：重庆交通大学, 2013.
GUO Kangsheng. The Study on Pavement Performance of the Different Mixing Rate Regeneration Mixture Based on Reference Material Synthesis［D］. Chongqing：Chongqing
Jiaotong University, 2013.
［14］徐剑,黄颂昌,邹桂连.高等级公路沥青路面再生技术［M］.北京:人民交通出版社, 2011: 1-10.
XU Jian, HUANG Songchang, ZOU Guilian. Recycling Technology of High Grade Asphalt Pavement［M］. Beijing: China Communications Press, 2011: 1-10.
［15］谭忆秋.沥青与沥青混合料［M］.哈尔滨:哈尔滨工业大学出版社, 2007: 57-62.
TAN Yiqiu. Asphalt and Asphalt Mixture［M］. Harbin: Harbin Institute of Technology Press, 2007: 57-62.
［16］査旭东,闵斌,宋微.RAP掺量对热再生沥青混合料性能影响分析［J］. 长沙理工大学学报（自然科学版）, 2013, 13(4): 1-7.
ZHA Xudong, MIN Bin, SONG Wei. Influence analysis of RAP content on performances of hot recycled asphalt mixture［J］. Journal of Changsha University of Science
and Technology （Natural Science), 2013, 10(4): 1-8.
［17］张争奇,李宁利,陈华鑫.改性沥青混合料拌合与压实温度确定方法［J］.交通运输工程学报, 2007, (7)2: 36-40.
ZHANG Zhengqi, LI Ningli, CHEN Huaxin. Determining method of mixing and compaction temperatures for modified asphalt mixture［J］. Journal of Traffic and
Transportation Engineering, 2007, 7 (2): 36-40.
［18］吴建涛,刘泉, 韩伟鹏.膜厚度对沥青流变性能的影响研究［J］.建筑材料学报, 2017, (20)2: 300-304.
WU Jiantao, LIU Quan, HAN Weipeng. Influence of film thickness on rheological properties of bitumen［J］. Journal of Building Materials, 2017, (20)2: 300-304.

[1]	张淑宝. 一种中央分隔带分离式改进混凝土护栏的研究[J]. 重庆交通大学学报（自然科学版）, 2021, 40(07): 107-111.
[2]	赵伟. 纳米蒙脱石/SBS复掺改性沥青性能试验研究[J]. 重庆交通大学学报（自然科学版）, 2021, 40(07): 118-122.
[3]	郭鹏1，陈思贤1，曹志国1，刘俊1，孟建玮2，鲜江林3. 复配废机油再生剂的制备及性能研究[J]. 重庆交通大学学报（自然科学版）, 2021, 40(06): 87-91.
[4]	肖庆一1,2，赵鹏1，孙博伟3，张怡4，丁啸5. 废植物油再生沥青结合料性能研究[J]. 重庆交通大学学报（自然科学版）, 2021, 40(06): 92-98.
[5]	何丽红1,2,温仙仙1,2,侯艺桐1,2,邓稳1,2. 阴离子乳化沥青粒径大小及分布影响因素分析[J]. 重庆交通大学学报（自然科学版）, 2021, 40(06): 99-104.
[6]	姚爱玲1，王军伟2，许敏3，杨孟乾4，杨涛1. 水泥稳定碎石基层沥青路面隆起开裂数值分析[J]. 重庆交通大学学报（自然科学版）, 2021, 40(06): 105-111.
[7]	赵全满，任瑞波，刘瑶，李志刚，户桂灵. 城市道路检查井井周路面破坏机理[J]. 重庆交通大学学报（自然科学版）, 2021, 40(05): 87-94.
[8]	王志祥1,2，李建阁1，陈楚鹏2. 基于变权重评价的沥青路面使用性能灰色预测[J]. 重庆交通大学学报（自然科学版）, 2021, 40(05): 95-101.
[9]	肖庆一1，2，3，封仕杰1，孙立东1，陈向伟1. 碱渣掺量对不同龄期下半刚性再生基层力学性能研究[J]. 重庆交通大学学报（自然科学版）, 2021, 40(05): 102-109.
[10]	潘兵宏1，2，任卉2，单慧敏1，霍永富1. 客货分离整体式路基互通出口同分带开口长度研究[J]. 重庆交通大学学报（自然科学版）, 2021, 40(04): 83-90.
[11]	孔令云1，邹胜楠1，黄麟钬2，吴海鹰3，余苗1，杨博1. 复合式路面疲劳裂纹扩展数值模拟研究[J]. 重庆交通大学学报（自然科学版）, 2021, 40(04): 91-97.
[12]	凌天清1，魏巧2，李传强3，袁海2，杨清尘3. 生物柴油-塑料裂解蜡复合温拌改性沥青性能研究[J]. 重庆交通大学学报（自然科学版）, 2021, 40(04): 98-104.
[13]	王清洲1，孙超1，檀奥龙2，魏连雨1. 膨胀性泥岩重塑土膨胀力试验研究[J]. 重庆交通大学学报（自然科学版）, 2021, 40(04): 112-117.
[14]	王民1,2，尚飞1，肖丽1，包广志3. 钢桥面浇注式沥青铺装复合梁疲劳损伤规律分析[J]. 重庆交通大学学报（自然科学版）, 2021, 40(03): 84-88.
[15]	董仕豪，韩森，尹媛媛，吴松，张启鑫. 基于表面能理论的石灰改性沥青黏附性研究[J]. 重庆交通大学学报（自然科学版）, 2021, 40(03): 89-97.