基于切削加固的钢桁梁桥横梁节点翼缘组合维修效果研究

doi:10.3969/j.issn.1674-0696.2023.02.05

摘要/Abstract

摘要： 采用有限元法建立了简支钢桁梁桥全桥模型及节点子模型；通过对比关键截面竖向位移及杆件轴向应力的实桥测试值与有限元计算值，验证了有限元模型的正确性；分析了不同裂纹长度裂纹尖端的应力强度因子KⅠ、KⅡ、KⅢ的变化规律；针对横梁节点腹板间隙疲劳开裂，分析了上翼缘切削方法及角钢加固方法的维修效果；提出了横梁端部上翼缘切削与角钢加固的组合维修方法。结果表明：裂纹在整个扩展过程中，开裂模式从Ⅱ-Ⅲ型开裂先向Ⅰ-Ⅱ-Ⅲ型开裂转变，再向Ⅱ-Ⅲ型开裂转变；上翼缘切削方法、角钢加固方法对Ⅰ型裂纹、Ⅱ型裂纹均具有较好的维修效果，组合维修方法对复合型裂纹具有较好的抑制作用；模型中当裂纹扩展长度小于腹板间隙长度的60%时，裂纹尖端等效应力强度因子可降低60%～90%，抑制效果显著。

关键词: 桥梁工程；钢桁梁桥；腹板间隙；疲劳开裂；应力强度因子

Abstract: A whole bridge model and node sub-model of simply supported steel truss bridge were established by the finite element analysis method. The correctness of the finite element model was verified by comparing the measured values with the calculated values of the finite element method of the key section vertical displacement and the axial stress of the member. The variation rules of stress intensity factors KⅠ, KⅡ, and KⅢ at the crack tip under different crack lengths were analyzed. Aimed at fatigue cracking of web gap in crossbeam joints, the maintenance effects of cutting the upper flange and angle steel reinforcement were analyzed. A combined maintenance method of cutting the upper flange of the beam end and strengthening the angle steel was proposed. The results show that the cracking mode changes from type Ⅱ-Ⅲ crack to type Ⅰ-Ⅱ-Ⅲ crack and then to type Ⅱ-Ⅲ crack during the whole process of crack propagation. The upper flange cutting method and angle steel reinforcement method have good repair effects on both type I and type Ⅱ cracks, and the combined maintenance method of the upper flange cutting and angle steel reinforcement has a good inhibitory effect on composite type cracks. In the proposed model, when the crack propagation length is less than 60% of the web gap length, the equivalent stress intensity factor at crack tip can be reduced by 60% to 90%, and the inhibiting effect is significant.

Key words: bridge engineering; steel truss bridge; web gap; fatigue cracking; stress intensity factor

中图分类号:

U441.4

李传喜，吉伯海，姚悦，傅中秋. 基于切削加固的钢桁梁桥横梁节点翼缘组合维修效果研究[J]. 重庆交通大学学报（自然科学版）, 2023, 42(2): 28-36.

LI Chuanxi, JI Bohai, YAO Yue, FU Zhongqiu. Repair Effect of Beam Joint Flange Combination of Steel Truss Bridge Based on Cutting Reinforcement[J]. Journal of Chongqing Jiaotong University(Natural Science), 2023, 42(2): 28-36.

参考文献

［1］ YU Xiangdong, DENG Yongle, YAN Bin. Case study of the 156 m simply supported steel truss railway bridge ［J］. Structural Engineering International, 2017, 27(4):563-568.
［2］王贤强, 杨羿, 刘朵, 等.节点板高强螺栓预紧力松弛试验研究［J］.钢结构,2019,34 (11):40-44.
WANG Xianqiang, YANG Yi, LIU Duo, et al. Experimental research on pre-tightening force relaxation of high-strength bolt in joint plate ［J］. Steel Construction, 2019,34 (11):40-44.
［3］《中国公路学报》编辑部.中国桥梁工程学术研究综述·2021［J］.中国公路学报,2021,34(2):1-97.
Editorial Department of China Journal of Highway and Transport. Review on Chinas bridge engineering research: 2021 ［J］. China Journal of Highway and Transport, 2021,34(2):1-97.
［4］ MOHAMMADI A, NAJJAR W S. Analytical study of fatigue cracking in coped stringers of steel bridges ［J］.Transportation Research Record, 2019, 2673(10): 239-246.
［5］夏晓东, 高日, 冯晓霞.带有裂纹构件的钢桁桥的检测和评估研究［J］.钢结构，2007，22(4)：81-83.
XIA Xiaodong, GAO Ri, FENG Xiaoxia. Study on detection and assessment for steel truss bridge with cracking members［J］. Steel Construction, 2007, 22(4): 81-83.
［6］刘兴文.某下承式钢桁梁桥荷载试验及分析［J］.公路交通技术, 2015 (4):116-118.
LIU Xingwen. Test and analysis of loads of some through steel truss bridge ［J］. Technology of Highway and Transport, 2015(4): 116-118.
［7］谭金华,曾国良,马凯龙.钢桁架桥疲劳开裂防控方法研究［J］.武汉理工大学学报(交通科学与工程版),2019,43(4):601-604.
TAN Jinhua, ZENG Guoliang, MA Kailong. Research on prevention and control methods of fatigue cracking for steel truss bridge［J］. Journal of Wuhan University of Technology (Transportation Science & Engineering) ,2019,43(4):601-604.
［8］ HAGHANI R, AL-EMRANI M, HESHMATI M. Fatigue-prone details in steel bridges ［J］. Buildings, 2012, 2: 456-476.
［9］崔鑫, 田越, 王丽, 等.既有铁路钢桥常见病害成因分析及强化对策研究［J］.铁道建筑,2016(9):10-13.
CUI Xin, TIAN Yue, WANG Li, et al. Cause analysis of common defects in existing railway steel bridges and corresponding strengthening measures［J］. Railway Engineering, 2016(9): 10-13.
［10］任伟平.焊接钢桥结构细节疲劳行为分析及寿命评估［D］.成都：西南交通大学，2008.
REN Weiping. Fatigue Behavior and Fatigue Life Evaluation of Structural Details in Welded Steel Girder Bridges ［D］. Chengdu: Southwest Jiaotong University, 2008.
［11］韩衍群, 叶梅新, 罗如登.整体桥面钢桁梁桥桥面荷载传递途径的研究［J］.铁道学报,2008,30(1):65-69.
HAN Yanqun, YE Meixin, LUO Rudeng. Study on the load transfer routine in truss bridges with integral decks［J］. Journal of the China Railway Society, 2008, 30(1): 65-69.
［12］ ALAMPALLI S, LUND R. Estimating fatigue life of bridge components using measured strains［J］. Journal of Bridge Engineering, 2006, 11(6): 725-736.
［13］ GUYER R C. Distortion-Induced Fatigue Investigation of Double Angle Stringer-to-Floorbeam Connections ［D］. Pennsylvania, USA: The Pennsylvania State University, 2010.
［14］ CONNOR R J, FISHER J W. Report on Field Inspection, Assessment, and Analysis of Floorbeam Connection Cracking on the Birmingham Bridge-Pittsburgh PA ［R］. Bethlehem PA, USA: Civil and Environmental Engineering, Lehigh University, 2001.
［15］舟山耕平, 杉本悠真, 山口隆司, 等.主構－床げたがボルト接合された床組構造を有する橋梁の疲労き裂に対する効果的な補修方法に関する研究：65A卷［G］∥構造工学論文集. 足利，日本：土木学会，2019：506-515.
FUNAYAMA K, SUGIMOTO Y, YAMAGUCHI T, et al. Study on effective reinforcement methods for fatigue cracks of floor beam which bolted to main structure: 65A ［G］∥ Journal of Structure Engineering. Ashikaga，Japan: JSCE, 2019: 506-515.
［16］ LIU Ming, FRANGOPOL D M, KWON K. Optimization of retrofitting distortion-induced fatigue cracking of steel bridges using monitored data under uncertainty ［J］. Engineering Structures, 2010, 32(11): 3467- 3477.
［17］ ROBERT J D, JUSTIN M O. Manual for Repair and Retrofit of Fatigue Cracks in Steel Bridges ［M］. New York, USA: Federal Highway Administration, 2013.
［18］ ROEDER C W, MACRAE G, CROCKER P, et al. Dynamic response and fatigue of steel tied-arch bridge［J］.Journal of Bridge Engineering, 2000, 5(1):14-21.
［19］ ROEDER C W, MACRAE G, LELAND A, et al. Extending the fatigue life of riveted coped stringer connections ［J］. Journal of Bridge Engineering, 2005, 10(1): 69-76.
［20］卜一之,金通,李俊,等.纵肋与横隔板交叉构造细节穿透型疲劳裂纹扩展特性及其加固方法研究［J］.工程力学,2019,36(6):211-218.
BU Yizhi, JIN Tong, LI Jun, et al. Research on propagation characteristics and reinforcement method of penetrating crack at rib-to-diaphragm welded joints in steel bridge deck［J］. Engineering Mechanics,2019,36(6):211-218.
［21］杨星星.中小跨径钢桁梁桥的静动力特性研究［D］.扬州：扬州大学，2018.
YANG Xingxing. Research on Static and Dynamic Characteristics of Medium and Small Span Steel Truss Girder Bridges ［D］. Yangzhou: Yangzhou University, 2018.
［22］童乐为,顾敏,朱俊,等.基于断裂力学的圆钢管混凝土T型焊接节点疲劳寿命预测［J］.工程力学,2013,30(4):331-336,354.
TONG Lewei, GU Min, ZHU Jun, et al. Prediction of fatigue life for welded T-joints of concrete-filled circular hollow sections based on fracture mechanics［J］. Engineering Mechanics, 2013, 30(4):331-336, 354.
［23］史国刚,吉伯海,陈壮壮,等.钢板梁桥腹板加劲肋焊缝疲劳开裂后的应力特征［J］.河海大学学报(自然科学版),2022,50(2):69-75.
SHI Guogang, JI Bohai, CHEN Zhuangzhuang, et al. Stress characteristics of web-stiffener weld after cracking in steel plate girder bridges ［J］. Journal of Hohai University (Natural Sciences), 2022, 50(2): 69-75.

[1]	吉伯海，徐捷，姚悦，傅中秋. 考虑荷载影响面的钢桥面板顶板-U肋焊缝疲劳损伤分析[J]. 重庆交通大学学报（自然科学版）, 2019, 38(11): 27-33.
[2]	张晓艳，汪富资，于辉，吴杰，唐亮. 基于面曲率变化的模型桥损伤识别方法研究[J]. 重庆交通大学学报（自然科学版）, 2019, 38(10): 33-40.
[3]	渠昱1，2，曾勇1，2，顾安邦1，2，杜柏松1，2. XFEM及其在正交异性钢桥面板疲劳裂纹扩展中的应用[J]. 重庆交通大学学报（自然科学版）, 2018, 37(04): 21-27.
[4]	刘山洪，魏建东，钱永久. 光纤传感器在桥梁监控中的应用分析[J]. 重庆交通大学学报（自然科学版）, 2005, 24(3): 4-7.
[5]	杜柏松，许振波，周文静，钟志权. 钢桥面横隔板弧形切口残余应力分布特性研究[J]. 重庆交通大学学报（自然科学版）, 2022, 41(01): 59-66.
[6]	姚悦，吉伯海，杨良泽，傅中秋. 钢板梁桥主梁腹板焊缝疲劳成因与构造优化分析[J]. 重庆交通大学学报（自然科学版）, 2022, 41(11): 81-88.