沥青与沥青组分的差示扫描量热研究

doi:10.3969 /j.issn.1674-0696.2013.02.08

摘要/Abstract

摘要： 采用沥青组分分析法和差示扫描量热仪( DSC) 从微观上分析沥青的性质。试验选取ESSO 90 # 基质沥青及RTFO( 旋转薄膜烘箱) /PAV( 压力老化) 基质沥青，研究了沥青的沥青质、饱和分、芳香分和胶质四组分。结果表明:DSC 能较好的描述沥青内部相态随温度的变化，并与沥青宏观上的三大指标保持一致; 沥青质、胶质对沥青的高温性能有影响，饱和分、芳香分对沥青的低温性能有影响; 饱和分对沥青性质的影响很大。

关键词: 沥青组分, 差示扫描量热仪, 老化

Abstract: Asphalt fraction analysis and DSC ( Differential Scanning Calorimetry) instrument were adopted to analyze the property of the asphalt from the microscopic． ESSO 90 # matrix asphalt and RTFO ( Rotary Film Oven) / PAV ( Pressure Aging) matrix asphalt were selected，and the asphalt four fractions ( asphaltene，saturates，aromatics，colloid) were studied during the test． The results show that: DSC can better describe internal phase state of asphalt changing with temperature，and remain consistent with the three major asphalt macro indicators; asphaltene and colloid affect the high temperature performance of asphalt． Saturates and aromatics affect the low temperature performance of asphalt; saturates has an significant impaction on asphalt property．

Key words: asphalt fraction, differential scanning calorimetry ( DSC) , aging

中图分类号:

U414

陈华鑫，贺孟霜，李媛媛，颜赫. 沥青与沥青组分的差示扫描量热研究[J]. 重庆交通大学学报（自然科学版）, 2013, 32(2): 207-0210.

Chen Huaxin，He Mengshuang，Li Yuanyuan，Yan He. DSC Analysis on Asphalt and Asphalt Fractions[J]. Journal of Chongqing Jiaotong University(Natural Science), 2013, 32(2): 207-0210.

参考文献

［1］王翠红，王子军，王红，等．沥青四组分测定条件对结果的影响［J］．石油沥青， 2009，23( 2) : 56-59． Wang Cuihong，Wang Zijun，Wang Hong，et al． The influenced factors to test results of asphalt four component［J］． Petroleum Asphale，2009，23 ( 2) : 56-59．［2］陈华鑫，陈拴发，王秉纲．基质沥青老化行为与老化机理［J］．合成材料老化与应用，2009，38( 1) : 13-19． Chen Huanxin，Chen Shuanfa，Wang Binggang． Aging behavior and mechanism of base asphalts ［J］． Synthetic Materials Aging and Application，2009，38( 1) : 13-19．［3］李洪峰，周子兵．对沥青化学组分分析方法的研究［J］．黑龙江交通科学，2004( 8) : 17-18． Li Hongfeng，Zhou Zibing． The research of asphalt chemical composition［J］． Heilongjiang Traffic Science，2004( 8) : 17-18．［4］伍真川．老化对沥青性能的影响［J］．公路与汽车，2004 ( 2) :62-63． Wu Zhenchuan． The influenced of asphalt aging ［J］． Highway ＆ Automotive Applications，2004( 2) : 62-63．［5］ Mostafa A E，Louay N M，Ionela G，et al． Relationship between molecular compositions and rheological properties of neat asphalt binder at low and intermediate temperatures ［J］． Journal of Materials in Civil Engineering，2010，22( 12) : 1288-1294．［6］ Felaniaina R，Hicham F，Parviz R，et al． Hexabenzocoronene model compounds for asphalt fractions: synthesis ＆ characterization ［J］． Energy and Fuels，2006，20: 2439-2447．［7］曾凡奇，黄晓明，李海军．沥青性能的DSC 评价方法［J］．交通运输工程学报，2005，5( 4) : 37-42． Zeng Fanqi，Huang Xiaoming，Li Haijun． Evaluation method of differential scanning calorimetry for asphalt performance［J］． Journal of Traffic and Transportation Engineering，2005，5 ( 4 ) : 37-42．［8］ William D H，Qiu Zhaoyao，Ioan N． Differential scanning calorimetry study of asphalt crystallite ［J］． Transportation Research Record，1996，1535: 54-60．［9］ Herrington P R，Ball G F A． Temperature dependence of asphalt oxidation mechanism［J］． Fuel，1996，75( 9) : 1129-1131．［10］ JT J 052—2000 公路工程沥青及沥青混合料试验规程［S］．北京: 人民交通出版社，2000．JT J 052—2000 Highway Engineering Asphalt and Asphalt Mixture Test Procedures［S］． Beijing: China Communications Press，2000

[1]	高桂海，郭宁，钱波. 沥青组分对沥青抗老化性能影响研究[J]. 重庆交通大学学报（自然科学版）, 2020, 39(04): 69-73.
[2]	张争奇，方滢，李卓琳. 脱硫橡胶沥青和普通橡胶沥青性能试验研究[J]. 重庆交通大学学报（自然科学版）, 2020, 39(04): 74-79.
[3]	朱洪洲，钟伟明，万逸秋，向浩，杨洋. 生物重油再生沥青物理性能试验研究[J]. 重庆交通大学学报（自然科学版）, 2018, 37(08): 23-28.
[4]	李嘉1,2，赵昭1，王万鹏1，陈卫1. 模拟自然条件下UHPC-TPO复合构件耐老化性能研究[J]. 重庆交通大学学报（自然科学版）, 2018, 37(07): 46-53.
[5]	陈龙1，朱建勇2，何兆益1，程永3，陈先勇4. 厂拌热再生沥青混合料低温抗裂与水稳定性研究[J]. 重庆交通大学学报（自然科学版）, 2017, 36(4): 38-44.
[6]	于江，李文博，李林萍. 纳米二氧化钛对沥青老化性能的影响研究[J]. 重庆交通大学学报（自然科学版）, 2017, 36(10): 26-30.
[7]	陈龙1，陈松敏2，何兆益1. 光热耦合条件下沥青宏观老化特征研究[J]. 重庆交通大学学报（自然科学版）, 2016, 35(6): 38-44.
[8]	唐伯明,袁颖,曹雪娟,田春玲,余苗. 沥青路面热反射涂料老化规律及其机理探讨[J]. 重庆交通大学学报（自然科学版）, 2015, 34(3): 47-51.
[9]	布海玲,刘涛,杨三强. 新疆地区常用沥青短期老化低温性能的评价[J]. 重庆交通大学学报（自然科学版）, 2015, 34(2): 50-53.
[10]	陈华鑫，贺孟霜，李媛媛，颜赫. 沥青与沥青组分的差示扫描量热研究[J]. 重庆交通大学学报（自然科学版）, 2013, 32(2): 207-210.
[11]	何兆益，欧祖敏，刘楠，陈宏斌. 加热温度和时间对沥青混合料老化的影响[J]. 重庆交通大学学报（自然科学版）, 2012, 31(2): 239-242.
[12]	郭韦韦，张祖棠. 高寒地区光老化对沥青混合料低温性能影响[J]. 重庆交通大学学报（自然科学版）, 2012, 31(1): 51-53.
[13]	欧阳君，孙大权，章毅. 基于流变性能的SBS 改性沥青老化动力性能研究[J]. 重庆交通大学学报（自然科学版）, 2011, 30(3): 411-414.
[14]	白洪涛, 王福敏. 桥梁改造工程寿命周期成本模型的建立与分析[J]. 重庆交通大学学报（自然科学版）, 2008, 27(2): 208-212.
[15]	吴欢，梁乃兴. SBR改性沥青混合料紫外光照老化分析[J]. 重庆交通大学学报（自然科学版）, 2007, 26(2): 72-74.