Abstract: Based on the TD-GC/MS online technique，the volatiles total ion current chromatogram of poplar powder composites which were formed by warm self-bonding compaction were analyzed at 40 ℃，60 ℃，90 ℃ and 160 ℃． The peak area normalization method was used to identify the retention time and peak area of poplar powder-based composites at each temperature， then the environment friendliness of poplar powder-based composites was evaluated． The results show that in the volatiles of poplar powder-based composites，the beneficial component content is significant higher than that of harmful component at each temperature． The beneficial components are 6 times higher than harmful components at 40 ℃，60 ℃ and 90 ℃，and the corresponding value at 160 ℃ is 29 times，so the environment friendliness is good． The total volatiles kinds， beneficial components kinds and harmful components kinds of poplar powder-based composite are approximately quite to that of poplar raw powder，but the beneficial component content increases evidently and the harmful component content decreases significantly． It shows that not only the warm self-bonding compaction process of poplar powder-based composites have environment friendliness，but also the preparation and application processes are environment friendly．

Key words: poplar powder-based composites, warm self-bonding compaction, TD-GC/MS, environment assessment

摘要： 在运用热脱附－气相色谱/质谱(TD－GC/MS)联机技术分析杨木粉末无胶温压成形复合材料在4，60，90 和160℃等4个环境温度点的挥发物总离子流图的基础上，采用色谱峰面积归一化法鉴定出杨木粉末基复合材 料在各温度下的保留时间及峰面积，进而评价杨木粉末基复合材料的环境友好性。结果表明:在不同温度下，杨 木粉末基复合材料挥发物中的有益成分含量明显多于有害成分，在40，60和160℃时，有益成分含量为有害成分 含量的6倍以上，90℃时有益成分为有害成分的29倍，环境友好性良好;杨木粉末基复合材料总挥发物种类及 有益成分种类、有害成分种类与杨木原粉相应种类大致相当，但有益成分明显增多，有害成分减少，增减幅度较 大。说明这类杨木粉末基复合材料不仅无胶温压成形工艺具有环境友好性，且其制品的制备和使用过程都具有 环境友好性。

关键词: 杨木粉末基复合材料, 无胶温压成形, 热脱附－气相色谱/质谱, 环保评估